| 1. | typical cure temperatures range from 125 to 175℃.
典型的固化温度范围从125175。 |
| 2. | Shrinkage stress was found to increase linearly with cure temperature .
我们发现收缩应力随固化温度直线增加。 |
| 3. | Curing temperature and time
养护温度和时间 |
| 4. | Rate of cure and final strength will depend on the resistance time at the cure temperature
固化比率及最终固化强度取决于在固化温度条件下所持续的固化时间。 |
| 5. | Influence of curing temperatures on drying shrinkage characteristics of portland cement mortar with high doping of fly ash
养护温度对高掺量粉煤灰硅酸盐水泥砂浆干缩性能的影响 |
| 6. | The influence of temperature is greater ; the testing is faster and the results is more sensitive at curing temperature 80
温度对砂浆膨胀影响较大，采用80碱溶液养护，试验更迅速，结果更敏感。 |
| 7. | Abstract : the influences of curing temperature and alkali contents of cement on expansion of mortar bars are investigated
文摘:研究了养护温度和水泥碱含量(质量分数,下同)与硅质集料砂浆试样膨胀的关系。 |
| 8. | Results showed that the curing temperature of this system was come down , and the mousiture - resistance of this adhesive was improved
实验结果表明，采用上述的方法，可以大大降低固化的起始温度，并对固化后产物的耐湿热性有一定的提高。 |
| 9. | Final cure temperature below 15 is not recommended for tank linings . if max . recoating interval is exceeded , please consult technical department for instructions
以下的固化温度不建议用于水箱内层。如果过了最大重涂间隔，施工前请咨询技术部门。 |
| 10. | Also the infrared ray absorbing properties of the treated fabric can be affected by use of different kind of nano - materials under different curing temperature and concentration
且纳米材料的浓度、种类、焙烘温度都会影响整理织物的红外线吸收性能。 |